Welding Electrode Aws A5.10 E6013

• Type: E (Carbon Steel Electrodes/ Low Alloy Steel Electrodes)
• Material: Steel Alloy
• Diameter: 1.6-5.0mm
• Length: 300-450mm
• Welding Core Type: Carbon Structural Steel
• Electrode Coating Type: Titanium
• Model NO.: HFX-E6013
• Slag Characteristic: Alkaline
• Stainless Steel Welding Rod Type: Non
• Welding Power: AC/DC
• Standard: Aws A5.1 E6013
• Transport Package: Pallet
• Specification: 1.6mm-5.0mm
• Trademark: WELDBST
• Origin: P. R. C.
• HS Code: 83111000
• Production Capacity: 50000tons/Year

Product Description

        E6013 is coated rutile type acid electrode, AC and DC both can be used and can be for all-position welding. It can reach excellent welding performance, stable arc, little spatter, easy slag removal and good weld appearance.

        Model No.:  AWS A5.1E6013 
         Diameter: 1.6mm, 2.0mm, 2.5mm, 3.2mm, 4.0mm, 5.0mm
         Net weight: 1, 2.5, 5 kg/box, 20 kg/carton, 1 ton/pallet

Application:
        It is suitable for welding low carbon steel structure, especially suitable for the welding of thin plate and short weld of discontinuous and covering welding which requires smooth surface.Widely used for welding of machineries, engineer machineries, ship building, bridges, pressure vessels, building constructions.

Chemical composition of welding electrode (%)

Item	C	Mn	Si	S	P	Cr	Ni	Mo	V
Samle value	0.080	0.43	0.21	0.020	0.026	0.011	0.04	0.007	0.009

Mechanical properties of deposited metal

Item	Tensile Strength Rm(Mpa)	Yield Strength REl(Mpa)	Elongation (%)	AKV Impact value (J)(20°C)
Samle value	490	396	26	82

Welding parameter(AC,DC)

Rod diameter(mm)	2.0	2.5	3.2	4.0	5.0
Current (A)	40-70	50-90	90-130	130-210	170-230

NOTICE:
        Normally, don't need to bake before welding electrode, when the electrode e affected with damp, it should be subject to use 150-170°C for 0.5-1 hour.